Three dimensional printing and biomaterials in the repairment of bone defects; hydroxyapatite pla filaments


Kaya İ., ŞAHİN M. C., Cingöz İ. D., AYDIN N., Atar M., KIZMAZOĞLU C., ...Daha Fazla

Turkish Journal of Medical Sciences, cilt.49, sa.3, ss.922-927, 2019 (SCI-Expanded) identifier identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 49 Sayı: 3
  • Basım Tarihi: 2019
  • Doi Numarası: 10.3906/sag-1901-184
  • Dergi Adı: Turkish Journal of Medical Sciences
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, TR DİZİN (ULAKBİM)
  • Sayfa Sayıları: ss.922-927
  • Anahtar Kelimeler: Bone tissue engineering, Filaments, Hydroxyapatite, PLA, Three dimensional printing
  • Uşak Üniversitesi Adresli: Evet

Özet

Background/aim: Application fields of bone tissue engineering studies continue to expand. New biocompatible materials aimed to improve bone repairment and regeneration of implants are being discovered everyday by scientists, engineers, and surgeons. Our objective in this study is to combine polylactic acid which is a polymer with hydroxyapatite in the repairment of bone defects considering the increased need by medical application fields. Materials and methods: After 750 g of PLA with a diameter of 2.85 mm was granulated into minimum particles, these particles were homogenously mixed with hydroxyapatite prepared in laboratory environment. Using this mixture, HA-PLA filament with a diameter of 2.85 mm was prepared in the extrusion device in Kütahya Medical Sciences University Innovative Technology Laboratory. The temperature was 250 °C and the gearmotor speed was 9 rpm during extrusion. X-ray diffraction (XRD) analysis was made for crystal phase analyses of the produced hydroxyapatite powder, to determine the produced main phase and examine whether a minor phase occurred. Vickers microhardness test was applied on both samples to measure the endurance levels of the samples prepared with HAPLA filament. A loading force of 10 kg was applied on the samples for 10 s. Results: Hydroxyapatite peaks in XRD spectrum of the sample presented in figures are concordant with Joint Committee on Powder Diffraction Standards, JCPDS - File Card No. 01-075-9526 and no significant minor phase was observed. For both samples, hardness value was observed to increase between 3 and 5 mm. Conclusion: Surfacing hydroxyapatite on metallic materials is possible. By similar logic, to increase durability with low cost, characteristics of biomaterials can be improved with combinations such as hydroxyapatite PLA. Thus, we found that while these materials have usage limitations due to present disadvantages when used alone, it is possible to increase their efficiency and availability through different combinations.