Bending characteristics of laminated wood composites made of poplar wood and gfrp Savojna svojstva lameliranog drva izrađenoga od topolovine i gfrp-a

Yildrim M. N., Karaman A., Zor M.

Drvna Industrija, cilt.72, sa.1, ss.3-11, 2021 (SCI-Expanded) identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 72 Sayı: 1
  • Basım Tarihi: 2021
  • Doi Numarası: 10.5552/drvind.2021.1913
  • Dergi Adı: Drvna Industrija
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, CAB Abstracts, Compendex, Environment Index, Geobase, Veterinary Science Database
  • Sayfa Sayıları: ss.3-11
  • Anahtar Kelimeler: Bending strength, Modulus of elasticity, Poplar, Wood laminate
  • Uşak Üniversitesi Adresli: Evet

Özet

• In this study, 4 layers of 5 mm thick slats obtained by sawing method from poplar wood were used. Plain woven GRFP with low density and grammage of 100 g/m2 (Type 1) and plain woven GRFP with high density and grammage of 200 g/m2 (Type 2) were placed and glued between each layer. Polyvinyl acetate (PVAc-D4), Polyurethane (PU) and dual-component Epoxy (L285-resin and H285-hardener) adhesives were used for gluing the layers. Strength values (bending and modulus of elasticity) between the obtained layers were investigated. As a result of the study, it was determined that epoxy glue has higher strength than polyurethane and polyvinyl acetate glues; Type 2 plain woven fabric has higher strength than Type 1 plain woven fabric; and parallel load to the glue line results in higher performance than perpendicular load to the glue line.