Engineering Failure Analysis, cilt.13, sa.8, ss.1260-1267, 2006 (SCI-Expanded)
This paper describes the failure analysis of a diesel engine crankshaft used in a truck, which is made from ductile cast iron. The crankshaft was found to break into two pieces at the crankpin portion before completion of warranty period. The crankshaft was induction hardened. An evaluation of the failed crankshaft was undertaken to assess its integrity that included a visual examination, photo documentation, chemical analysis, micro-hardness measurement, tensile testing, and metallographic examination. The failure zones were examined with the help of a scanning electron microscope equipped with EDX facility. Results indicate that fatigue is the dominant mechanism of failure of the crankshaft. It was observed that the fatigue cracks initiated from the fillet region of the crankpin-web. The absence of the hardened case in the fillet region and the presence of free graphite and nonspheroidal graphite in the microstructure of the crankshaft made fatigue strength decrease to lead to fatigue initiation and propagation in the weaker region and premature fracture. © 2005 Elsevier Ltd. All rights reserved.